這是美標牌號，對應(yīng)的國內(nèi)牌號沒有，最接近的是Y15,Y13, 但是不能等同，這種材料多為進口。
1215鋼材 1215易切削鋼為環(huán)保料,與12L14相比不含鉛及不含有對環(huán)境有害物質(zhì),切削性良好.適合一般電鍍軸心、切削用料及一般零件.1215由于精度準確,表面狀況良好,易削切鋼產(chǎn)品可直接使用,如噴涂,打砂,打彎,鉆孔,也可按實際要求精拉之后直接電鍍,免去了大量機加工時間及節(jié)省配置加工機械的費用.
1215鋼材用途：
主要用于制作受力較小而對尺寸和光潔度要求嚴格的儀器儀表、手表零件、汽車、機床和其他各種機器上使用的，對尺寸精度和光潔度要求嚴格，而對機械性能要求相對較低的標準件，如齒輪、軸、螺栓、閥門、襯套、銷釘、管接頭、彈簧座墊及機床絲杠、塑料成型模具、外科和牙科手續(xù)用具等。
1215鋼材化學(xué)成份(%):
C :≤0.09
Mn :0.75-1.05
P :0.04-0.09
S :026-0.35
易切削鋼AISI1215的化學(xué)成分/%
C : 0.06-0.10
Si<0.15
Mn:0.90-1.10
P:0.05-0.08
S :0.27-0.35
Pb：0-0.35
O：0.01-0.03
N：0.002-0.007
| AISI 1215 |
 |
|
| Category | Steel |
| Class | Carbon steel |
| Type | Standard resulfurized and rephosphorized |
| Designations | United States: ASTM A108 , ASTM A29 , FED QQ-S-637 , SAE J412 , UNS G12150 |
| Composition |
|
 |
| Mechanical Properties |
|
|
| Properties | Conditions |
| T (°C) | Treatment |
| Density (×1000 kg/m3) | 7.7-8.03 | 25 |
|
| Poisson's Ratio | 0.27-0.30 | 25 |
|
| Elastic Modulus (GPa) | 190-210 | 25 |
|
| Tensile Strength (Mpa) | 540 | 25 | cold drawn (round bar (19-38 mm)) |
| Yield Strength (Mpa) | 415 |
| Elongation (%) | 10 |
| Reduction in Area (%) | 35 |
| Hardness (HB) | 167 | 25 | cold drawn (round bar (19-38 mm)) |
| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 | cold drawn (round bar (19-38 mm)) | Tensile Strength (MPa) | 540 |
| Yield Strength (MPa) | 415 |
| Elongation (%) | 10 |
| Reduction in Area (%) | 35 |
| 25 | hot rolled (round bar (19-38 mm)) | Tensile Strength (MPa) | 525 |
| Yield Strength (MPa) | 470 |
| Elongation (%) |
|
| Reduction in Area (%) |
|
| 25 | turned and polished (round bar (19-38 mm)) | Tensile Strength (MPa) | 385 |
| Yield Strength (MPa) | 230 |
| Elongation (%) | 25 |
| Reduction in Area (%) | 45 |
| Conditions | Hardness |
| T (°C) | Treatment | Method | Value |
| 25 | cold drawn (round bar (19-38 mm)) | HB | 167 |
| 25 | turned and polished (round bar (19-38 mm)) | HB | 121 |